Highly polished YSZ (Yttrium stabilized ZrO2) zirconium oxide jars has the performance of high wear resistance. Its hardness is 60 times the hardness of ordinary steel, highly wear-resistant and resistant to acid and solvents. The grinding jars are extensively applied on in the fields of Paint, Ink,Coating, Geology, Metallurgy, Electronics, Construction Material, Ceramics, Chemical Engineering, Light Industry, Medicine, Environmental Protection and so on. Each jar set includes grinding jar, jar lid, rubber sealing gasket and different sizes of mixed zirconium oxide grinding balls.
Item | Parameter |
Material | 5wt%Y2O3+95wt%Zro2 |
Crystal structure | High temperature hexagonal ,low temperature tetragonal |
Bending strength (Mpa) 20C | 200-300 |
Density (g/cm3) | 6.04 |
Fracture toughness KIC 20C (Mpa m1/2) | 2.3 |
Hardness (HV) 20C | 1000 |
Thermal conductivity W/mk | 27 |
Specific heat (J/g/k) | 0.45 |
Thermal expansion coefficient *106/C 20C-100C | 10 |
Melting point | 2715℃ |
Temperature range | 0~2300℃ |
Applicable environment | Ingot furnace and corrosive gas furnace |
Technical Data
Jar Volume
Volume | OD (mm) | ID (mm) | Height (mm) |
50ml | 55 | 38 | 67 |
100ml | 65 | 50 | 75 |
250ml | 92 | 74 | 88 |
500ml | 100 | 84 | 118 |
1000ml | 128 | 108 | 150 |
1.5L | 132 | 112 | 175 |
2.0L | 158 | 138 | 162 |
3.0L | 158 | 138 | 220 |
4.0L | 205 | 175 | 231 |
5.0L | 192 | 170 | 254 |
Choice of Grinding Jars&Grinding Ball
In order to prevent excessive abrasion, the hardness of the grinding jars used and of the grinding balls must be higher than that of the material used. Normally, grinding jars and grinding balls of the same material should be chosen.
Features
1. High specific gravity, high efficiency
2. Highly wear resistant to acid and solvents
3. High cost-effective, low wear and long lifetime
4. Highly polished, smooth, easy to clean, low abrasion to the equipment
5. High mechanical strength, good toughness, impact resistance, no broken beads
6. Mainly used for lab planetary ball mill machines